Ultramid® C3U
Polyamide 66/6 Copolymer
BASF Corporation
产品说明：
Ultramid C3U is an injection molding, general purpose PA6/66 grade with improved flame retardance. The product is UL recognized as 94V0 at 0.4 mm minimum thickness.
Applications
It is used for impact resistant electrical insulating parts such as contact bases and plug connector strips.
物性信息：
| 基本信息 |
|
| 黄卡编号 |
|
| 特性 |
|
| 用途 |
|
| 机构评级 |
|
| RoHS 合规性 |
|
| 形式 |
|
| 加工方法 |
|
| 多点数据 |
- Creep Modulus vs. Time (ISO 11403-1)
- Isochronous Stress vs. Strain (ISO 11403-1)
- Isothermal Stress vs. Strain (ISO 11403-1)
- Secant Modulus vs. Strain (ISO 11403-1)
- Shear Modulus vs. Temperature (ISO 11403-1)
- Viscosity vs. Shear Rate (ISO 11403-2)
|
| 物理性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 比重 |
1.16 |
-- |
g/cm³ |
ASTM D792, ISO 1183 |
| 溶化体积流率（MVR） (275°C/5.0 kg) |
140 |
-- |
cm³/10min |
ISO 1133 |
| 收缩率 - 流动 (3.18 mm) |
0.80 |
-- |
% |
|
| 吸水率 |
|
|
|
|
| 饱和 |
8.5 |
-- |
% |
ASTM D570 |
| 饱和, 23°C |
8.5 |
-- |
% |
ISO 62 |
| 平衡, 50% RH |
2.9 |
-- |
% |
ASTM D570 |
| 平衡, 23°C, 50% RH |
2.9 |
-- |
% |
ISO 62 |
| 硬度 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 球压硬度 |
100 |
-- |
MPa |
ISO 2039-1 |
| 机械性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 拉伸模量 (23°C) |
3500 |
1500 |
MPa |
ISO 527-2 |
| 抗张强度 |
|
|
|
|
| 屈服, 23°C |
83.0 |
-- |
MPa |
ASTM D638 |
| 屈服, 23°C |
75.0 |
45.0 |
MPa |
ISO 527-2 |
| 伸长率 |
|
|
|
|
| 屈服, 23°C |
5.0 |
-- |
% |
ASTM D638 |
| 屈服, 23°C |
4.0 |
18 |
% |
ISO 527-2 |
| 断裂, 23°C |
50 |
-- |
% |
ASTM D638 |
| 标称拉伸断裂应变 (23°C) |
6.0 |
> 50 |
% |
ISO 527-2 |
| 弯曲模量 (23°C) |
3000 |
-- |
MPa |
ASTM D790, ISO 178 |
| 冲击性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 简支梁缺口冲击强度 |
|
|
|
ISO 179 |
| -30°C |
4.0 |
-- |
kJ/m² |
ISO 179 |
| 23°C |
9.0 |
35 |
kJ/m² |
ISO 179 |
| 简支梁无缺口冲击强度 (23°C) |
80 kJ/m² |
无断裂 |
|
ISO 179 |
| 悬壁梁缺口冲击强度 |
|
|
|
|
| -40°C |
32 |
-- |
J/m |
ASTM D256 |
| 23°C |
43 |
-- |
J/m |
ASTM D256 |
| 23°C |
4.5 |
-- |
kJ/m² |
ISO 180 |
| 热性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 载荷下热变形温度 |
|
|
|
|
| 0.45 MPa, 未退火 |
224 |
-- |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
91.0 |
-- |
°C |
ASTM D648 |
| 1.8 MPa, 未退火 |
70.0 |
-- |
°C |
ISO 75-2/A |
| 熔融峰值温度 |
243 |
-- |
°C |
ASTM D3418, ISO 3146 |
| 线形热膨胀系数 |
|
|
|
|
| 流动 |
4.0E-5 |
-- |
cm/cm/°C |
ASTM E831 |
| 流动 |
8.0E-5 |
-- |
cm/cm/°C |
|
| 横向 |
9.0E-5 |
-- |
cm/cm/°C |
|
| RTI Elec |
|
|
|
UL 746 |
| 0.380 mm |
110 |
-- |
°C |
UL 746 |
| 0.750 mm |
120 |
-- |
°C |
UL 746 |
| 1.50 mm |
120 |
-- |
°C |
UL 746 |
| 3.00 mm |
120 |
-- |
°C |
UL 746 |
| RTI Imp |
|
|
|
UL 746 |
| 0.380 mm |
65.0 |
-- |
°C |
UL 746 |
| 0.750 mm |
105 |
-- |
°C |
UL 746 |
| 1.50 mm |
105 |
-- |
°C |
UL 746 |
| 3.00 mm |
105 |
-- |
°C |
UL 746 |
| RTI |
|
|
|
UL 746 |
| 0.380 mm |
65.0 |
-- |
°C |
UL 746 |
| 0.750 mm |
115 |
-- |
°C |
UL 746 |
| 1.50 mm |
120 |
-- |
°C |
UL 746 |
| 3.00 mm |
120 |
-- |
°C |
UL 746 |
| 电气性能 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| 体积电阻率 |
|
|
|
|
| 1.50 mm |
1.0E+13 |
1.0E+9 |
ohms·cm |
ASTM D257 |
| -- |
1.0E+13 |
1.0E+9 |
ohms·cm |
IEC 60093 |
| 介电强度 |
32 |
28 |
kV/mm |
IEC 60243-1 |
| 介电常数 (1 MHz) |
3.60 |
6.00 |
|
IEC 60250 |
| 耗散因数 (1 MHz) |
0.020 |
0.30 |
|
IEC 60250 |
| 漏电起痕指数 |
600 |
600 |
V |
IEC 60112 |
| 可燃性 |
干燥 |
调节后的 |
单位制 |
测试方法 |
| UL 阻燃等级 |
|
|
|
UL 94 |
| 0.380 mm |
V-0 |
-- |
|
UL 94 |
| 0.750 mm |
V-0 |
-- |
|
UL 94 |
| 1.50 mm |
V-0 |
-- |
|
UL 94 |
| 3.00 mm |
V-0 |
-- |
|
UL 94 |
| 注射 |
干燥 |
单位制 |
|
| 干燥温度 |
80.0 |
°C |
|
| 干燥时间 |
2.0 到 4.0 |
hr |
|
| 建议的最大水分含量 |
0.15 |
% |
|
| 加工（熔体）温度 |
240 到 285 |
°C |
|
| 模具温度 |
65.0 到 80.0 |
°C |
|
| 注塑压力 |
3.50 到 12.5 |
MPa |
|
| 注射速度 |
快速 |
|
|